409L Stainless Steel Coil

Cold rolled 409L stainless steel coil begins to crystallize after pouring, the supercooling degree of the liquid phase is largely due to direct contact with the surface of the crystallizer, and at the same time, the surface of the crystallizer promotes non-spontaneous nucleation. Therefore, the nucleation rate of the liquid phase is high and the formation rate is high.

409L Stainless Steel Coil

409/409l cold rolled stainless steel begins to crystallize after pouring, the supercooling degree of the liquid phase is largely due to direct contact with the surface of the crystallizer, and at the same time, the surface of the crystallizer promotes non-spontaneous nucleation. Therefore, the nucleation rate of the liquid phase is high and the formation rate is high.

Fine equiaxed crystals on the surface. The formation of fine equiaxed grains on the surface is rapid, and the carbides of titanium are too short to precipitate.

Thickness	0.2mm – 8.0mm, etc.
Width	600mm – 2000mm, the narrowed products pls check in strip products
Max coil weight	25MT, etc.
Coil ID	508mm,610mm, etc.
Finish	2B, 2D, BA, No.4, HL, Mirror, 8k, Emboss, Etch, etc.
Packaging	Wooden pallets, waterproof paper
Service	Samples and MTC can be provided as per your requirements.
Origin	China (Mainland)
Mill	TISCO, YUSCO, LISCO, JISCO, POSCO, ZPSS, QPSS, Baosteel, etc.

Chemical composition
Grade	C	Si	Mn	Cr	Ni
304	≤0.07	≤1.00	≤2.0	18.00~20.00	8.00~10.50
304L	≤0.030	≤1.00	≤2.0	18.00~20.00	9.00~13.00
310S	≤0.08	≤1.00	≤2.0	24.00~26.00	19.00~22.00
316	≤0.08	≤1.00	≤2.0	16.00~18.00	10.00~14.00
316L	≤0.03	≤1.00	≤2.0	16.00~18.00	12.00~15.00
321	≤0.08	≤1.00	≤2.0	17.00~19.00	9.00~13.00
904L	≤0.02	≤1.00	≤2.0	19.00~23.00	23.00~28.00
2205	≤0.03	≤1.00	≤2.0	22.00~23.00	4.5~6.5
2507	≤0.03	≤0.08	≤1.20	24.00~26.00	6.00~8.00

409L Stainless Steel Coil